Product Name |
High Tensile Strength Steel Electrode |
Product No. |
MHAE411-WE012 |
Standard |
GB |
E5010 |
AWS |
E7010-G |
Type of Covering |
High cellulose Sodium |
Welding Position |
F,VD,OH,H |
Chemical Composition of Deposited Metal (%) |
Chemical Composition |
C |
Mn |
Si |
S |
P |
Ni |
Mo |
Cr |
V |
Guarantee |
— |
— |
— |
≤0.035 |
≤0.040 |
— |
— |
— |
— |
Mechanical Properties of Deposited Metal |
Test Item |
Tensile Strengh
Rm (MPa) |
Yield Point
ReL (MPa) |
Elongation
A4 (%) |
Akv1(J) |
Guarantee |
≥490 |
≥400 |
≥20 |
-30℃≥27 |
Reference Current(AC/DC) |
Electrode Diameter(mm) |
Electrode Length(mm) |
Welding Current(A) |
F |
H |
OH |
VD |
2.5 |
350 |
60-90 |
60-90 |
60-90 |
60-90 |
3.2 |
350 |
70-110 |
70-110 |
60-100 |
60-100 |
4.0 |
350 |
100-140 |
100-140 |
110-150 |
110-150 |
5.0 |
350 |
140-180 |
140-180 |
150-200 |
150-200 |
Instructions |
1.The Electrodes must be baked under 300~350 for an hour before Welding and used as soon as baking is completed. |
2.The stains on the weldments,such as rust,oil stains,moisture,etc.,must be cleared away before Welding. |
3.When Welding,short arc must be used and stringer bead is suitable. |
Application |
Used for Welding carbon steel and low-alloy steel structures,such as such as boilers,pressure vessels,pipelines and so on etc. |