Product Name | Stainless Steel Electrode | |||||||||
Product No. | MMDE411-WE059 | |||||||||
Standard | ||||||||||
GB | AWS | JIS | DIN | |||||||
E316-16 | E316-16 | D316 | E19123R26 | |||||||
Type of Covering | Lime titania | |||||||||
Welding Position | F,V, OH,H | |||||||||
Chemical Composition of Deposited Metal (%) | ||||||||||
Chemical Composition | C | Mn | Si | S | P | Cr | Ni | Mo | V | Cu |
Standard | ≤0.08 | 0.50-2.50 | ≤0.90 | ≤0.030 | ≤0.040 | 17.0-20.0 | 17.0-20.0 | 2.00-3.00 | ≤0.75 | — |
Typical | 0.037 | 0.82 | 0.64 | 0.013 | 0.028 | 18.81 | 12.00 | 2.50 | 0.19 | — |
Mechanical Properties of Deposited Metal | ||||||||||
Test Item | Tensile Strengh Rm (MPa) | Elongation A4 (%) | ||||||||
Standard | ≥520 | ≥30 | ||||||||
Typical | 575 | 42 | ||||||||
Reference Current (AC or DC) | ||||||||||
Electrode Diameter(mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 | |||||
Length(mm) | 300 | 300 | 350 | 400 | 400 | |||||
Instructions |
||||||||||
1.The Electrodes must be baked under 300-350℃for an hour before Welding. |
||||||||||
2.The weldment must be preheated to 250-350℃ before Welding. |
||||||||||
3.Try to use small current welding and short arcs ,the swinging width no more than the diameter of 2.5 times.
|
||||||||||
Application |
||||||||||
Suitable for 06Cr17Ni12Mo2 & Cr18Ni12Mo2 stainless steel structures for organic acid or inorganic acid mediums. Also it could be used in high Cr steel or dissimilar steels that cannot be PWHT. |